Removal of hydrocarbons and heavy metals from petroleum water by modern green nanotechnology methods

Scientific Reports volume 13, Article number: 5637 (2023) Cite this article

2376 Accesses

1 Citations

Metrics details

Considered heavy metals, such as As(III), Bi(II), Cd(II), Cr(VI), Mn(II), Mo(II), Ni(II), Pb(II), Sb(III), Se(-II), Zn(II), and contaminating chemical compounds (monocyclic aromatic hydrocarbons such as phenolic or polycyclic derivatives) in wastewater (petrochemical industries: oil and gas production plants) are currently a major concern in environmental toxicology due to their toxic effects on aquatic and terrestrial life. In order to maintain biodiversity, hydrosphere ecosystems, and people, it is crucial to remove these heavy metals and polluting chemical compounds from the watery environment. In this study, different Nanoparticles (α-Fe2O3, CuO, and ZnO) were synthesized by green synthesis method using Portulaca oleracea leaf extract and characterized by UV–Vis spectrophotometers, FTIR spectroscopy, X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Energy Dispersive Spectroscopy (EDS) techniques in order to investigate morphology, composition, and crystalline structure of NPs, these were then used as adsorbent for the removal of As(III), Bi(II), Cd(II), Cr(VI), Mn(II), Mo(II), Ni(II), Pb(II), Sb(III), Se(-II), and Zn(II) from wastewater, and removal efficiencies of were obtained 100% under optimal conditions.

The massive amount of water waste produced during the extraction of crude oil is known as produced water. It consists of oil well injection water mixed with formation water that is already present in the well. Produced water dissolves solids and suspended solids and contains a high oil concentration. This research is interested in treating the resulting water from the ALGERIA South oil company1.

In the oil industry, the growing demand for crude oil leads to very significant discharges causing irreversible and irreparable damage to nature and the environment. Among these discharges, we can cite the deposit waters accompanied by crude oil which are obtained at the level of the separator at the exit of oil wells, characterized essentially by high levels of hydrocarbons as well as by high levels of suspended solids and Heavy metals2. These metals are resistant to environmental degradation, difficult to metabolize, and have the potential to build up in the food chains of humans or ecosystems through ingestion3.

To fight effectively against these pollution problems, the consequences of which are varied, several solutions have been put forward by researchers in this field but require colossal means that the oil companies must take charge of. Among the solutions, it is to characterize, treat and valorize this deposit water by eliminating heavy metals and avoiding the formation of sloughs, a source of groundwater pollution4.

Currently, there are ways to treat water from the oil and gas industries with expensive raw materials, with a huge cost of producing treated water for possible reuse5. As an indication, these processes have certain limitations such as the inability to eliminate certain elements and the production of secondary waste requiring additional treatment. The goal of this project is to manufacture compounds of nanometric size, locally at a lower cost, and having high performance to eliminate waste of different types and sizes.

In today's world, researchers and scientists are increasingly interested in inorganic nanoparticles, especially oxides, as they are considered a scientific pillar thanks to their representation of modern scientific and technological achievements6,7. Metal oxide nanoparticles have been widely employed in a variety of applications, such as silver, iron, copper, gold, and oxide nanoparticle Such as iron oxide (hematite α-Fe2O38, magnetite Fe3O49), zinc oxide10,11, and copper oxide (cuprous oxide Cu2O12, and cupric oxide CuO13), It has been widely used in many different applications in materials engineering, biochemistry, and medicine14,15. These nanoparticles, hematite (α-Fe2O3), zinc oxide, and cupric oxide (CuO) nanoparticles have piqued the interest of researchers because of their unusual structural, optical, and catalytic capabilities, large surface area, and corrosion resistance making them a promising choice for catalysis and biological applications16. (α-Fe2O3, CuO, and ZnO) nanoparticles were reckoned to be efficient and can serve as drug carriers. Also, (α-Fe2O3, CuO, and ZnO) nanoparticles have a variety of medical applications, such as antibacterial, antifungal, anti-cancer, and anti-diabetic activities.

The inductively coupled plasma mass spectrometry technique was used to demonstrate the adsorption and elimination capacity of heavy metals present in the reservoir water by the various adsorbents: ZnO, α-Fe2O3 and CuO NPs. In addition, the field water is a gold mine that could contain up to 60% of unexploited crude oil and could be used in various industrial fields17,18.

The photocatalytic degradation of oily water (OIW) saturated of hydrocarbon and total suspended solids (TSS) of waste-water associated with crude oil production was studied using several nanoparticles α-Fe2O3, CuO, and ZnO, prepared by green synthesis. In addition to removing heavy metals. X-ray diffraction (XRD), scanning electron microscope (SEM), and Fourier transforms infrared spectroscopy (FTIR) were used for nanoparticle characterization. These nanoparticles have been found to be very efficient and the total photo mineralization of these organics to carbon dioxide and water occurs in air-equilibrated solution within 1 h.

Portulaca oleracea L. leaves were collected from El Oued, Southeast Algeria, the experimental research conducted in this study comply with relevant institutional, national, and international guidelines and legislation for research on plant material. Zinc Acetate (Zn (CH3COO)2· 2H2O, 98%), Ferric chloride (FeCl3·6H2O, 98%), Copper sulfate (CuSO4.5H2O, 98%) were purchased from Sigma-Aldrich, Germany. Distilled water was used in all the experiments.

First, 250 g fresh and collected Portulaca oleracea leaves from local farms in the El-Oued region (southeast of Algeria) were washed with tap water to get rid of dirt and organic deposits on the leaves and then rinsed repeatedly with demineralized water, then crushed and filtered. Fresh leaf components are extracted by mixing 250 g of leaves with 900 ml of distilled water in a 1000 mL glass beaker. The mixture was stirred for 15 min at room temperature. Then filter it using the decanting method and keep the extract cool by storing it at 4 °C for further use19,20,21.

Modified protocols from previous studies were used for the synthesis of α-Fe2O3, ZnO, and CuO NPs by a green method using plant extract22,23. For the synthesis of α-Fe2O3, ZnO, and CuO NPs. Different solutions of mineral salts (Ferric chloride (FeCl3·6H2O), Zinc Acetate (Zn(CH3COO)2·2 H2O), and copper sulfate (CuSO4.5H2O)) were prepared using distilled water. About 10 mL of every concentration was mixed with 1 mL of the Portulaca oleracea leaves extract with continuous stirring. With controlled and continuous stirring (600 rpm) at 70 °C for 2 h, the color of the solution changes. The precipitate was then centrifuged and washed several times with de-ionized water and dried at 100 °C in an oven for 48 h. Finally, the α-Fe2O3, ZnO, and CuO NPs were grinded into a fine powder24,25 .

The final solid product was collected using centrifugation and washed several times well with distilled water. The product was dried over night at 100 °C then is heated in a furnace at 500 °C for 3 h. The resulting powders were stored in containers for different characterizations26,27,28.

An all-purpose characterization method called UV–Vis spectroscopy is used to check optical characteristics including transparency and band gap. Shimadzu UV–Vis spectrophotometer model 1800, operating in the 200–900 nm wavelength range, is the instrument. Distilled water was employed as a reference solvent throughout the analysis of the samples in a quartz cell. The existence of functional groups in the chemical extract of the leaves was first ascertained using Fourier transform spectroscopy, and then the composition of α-Fe2O3, ZnO, and CuO NPs linkages was studied following calcination at 500 °C. The ATR instrument was utilized in the 4000–400 cm−1 range. By utilizing an X-ray diffractometer (Rigaku Miniflex 600) with a Cu-K (= 1.5406 ) in the 2 range of 10–90°, while X-ray was produced with 30 kilovolts and at 20 mA, the structure and grain size of α-Fe2O3, ZnO, and CuO were studied. Scanning electron microscopy (SEM) with energy dispersive X-ray spectroscopy was used to analyze the morphology and form of the nanoparticles (EDAX).

ICP-MS (Inductively Coupled Plasma Mass Spectrometry) the most sensitive method for determining the proportion of metals. It allows simultaneous identification of different ions in the same solution.

ICP-MS product HTDS, Model NexION 2000, it consists essentially of Water-cooled spray chamber, gas mass flow regulator (nebulizer gas, plasma gas and auxiliary gases), nebulizer with variable speed peristaltic pump, valve system and 0.5 mL injection loop, extractor for evacuating impurities, automatic sampler fitted with an injection system, syngetix operating software, 20 mL polypropylene conical tubes with polypropylene caps, Argon and helium gas supply cylinders at 99.9999% purity each, Ultra-pure water, multi-element stock standard solution, each element at a concentration of 1000 mg/litre, Mono-elemental standard solutions, Solutions of the reference element (internal standard) or optimization solution for the standard mode and for the KED mode (Kinetic energy discrimination).

Adsorbents Particles of iron oxide (α-Fe2O3), copper oxide (CuO) and zinc oxide (ZnO) synthesized by the green method.

TD-500D Oil in Water Meter the analyzer (Revision: C, P/N 100,668) from the United States of America uses UV fluorescence to determine the oil content of oily water comprising crude oil or gas condensates.

An oil in water analyzer (TD-500, Turner Designs Hydrocarbon Instruments, USA) was used to determine the amount of oil or OIW in the generated or separated water.

UV–Visible spectrophotometer Suspended solids (SS) represent all of the insoluble residues visible to the naked eye and suspended in the water. These materials can be analyzed by a UV–Visible spectrophotometer (brand mat-lib DR6000)—A test sample of 10 mL of petroleum water.

Oily water discharged by the separation units of crude oil extracted from the oil fields of the HASSI MESSAOUD area located in the south of Algeria (31.201183,5.740473).

Sorption studies were performed for eleven different metal As, Be, Cd, Cr, Mn, Mo, Ni, Pb, Sb, Se and Zn. All metal ions were taken in their nitrate form so that the effect of counter ion will be same29. To study the loading capacity of these metal ions on α-Fe2O3 CuO and ZnO NPs, 20 mg of NPs was taken and 10 mL oily water. Solution of different concentrations of metal ions were added. The solution was sonicated for 30 min followed by separation using a magnet and supernatant was analysed for metal ions concentration using ICPMS. A schematic diagram of the study is shown in Fig. 8. The results are obtained directly using the software integrated into the ICP device (Syngetix operating software.), they are calculated in mg/L using a linear regression of the response of the standards and are corrected by internal standards. If necessary, the data should be reintegrated following the software program. If applicable, multiply by the dilution factor.

A standard sample is used to calibrate the TD-500 m before analyzing a sample. As a first step, standard samples of known oil content are prepared. We put 100 mL of water in a bottle to analyze and adjust the pH at a value of < 2 with HCl (4 or 5 drops). After adding 10 mL of solvent (hexane) and shaking vigorously for 2 min, the hydrocarbons in the water were extracted. Let settle for about 10 min and fill with a syringe 3/4 of a bowl with the test socket extracted from the ampoule and wipe it clean. Place the bowl in the device and read the response value. The analyzer responds within 5 s. Note the concentration of hydrocarbons in ppm30,31.

A volume of 10 mL of petroleum water is poured into a transparent tank to allow the light beam to pass through the sample. The cuvette is then placed in the UV–VISIBLE spectrophotometer. The analysis is started. After 10 min the reading is made on the screen of the device32,33.

Portulaca oleracea communément appelée pourpier potager, elle est connue sous le nom arabe "Redjila". Le genre Portulaca comprend environ 40 espèces de tropicales et des espèces de climat chaud Portulaca oleracea L.

The leaves of Portulaca oleracea contain: alpha-linoleic acid, alpha-tocopherol and ascorbic acid with a very large amount than the leaves of spinach34.

The Fig. 1 exhibits typical XRD patterns of synthesized and annealed at 500 °C α-Fe2O3, CuO and ZnO nanoparticles, the sample of α-Fe2O3 shows very thin peaks, indicating the fine nature and small crystallite size of the particles . Show in Fig. 1 the spectrum indicate the presence of Hematite α-Fe2O3. As depicted by the peaks at 2θ values of 24.13°, 33.15°, 35.45°, 40.70°, 49.47°, 54.04°, 62.90° and 63.98° which correspond to the crystal planes of (012), (104), (110), (113), (024), (116) , (214) and (300) of Hematite a-Fe2O3 phase35 .All the reflection peaks are matching well with the expected to rhombohedral structure of α-Fe2O3 (space group: R-3c), respectively. Those planes accord well with the (JCPDS Card N°. 01–079-0007).

X-ray diffraction patterns of the α-Fe2O3, CuO and ZnO nanoparticles.

Figure 1 illustrates the XRD pattern of the cupric oxide (CuO) NPs prepared using Portulaca oleracea L. extract. The presence of cupric oxide crystals is confirmed by this diffractogram (CuO). Peaks position with 2θ values of 32.5°, 35.5°, 38.8°, 48.8°, 58.3°, 61.7°, 66.3°, and 68.4° correspond to the crystalline planes of (110), (002), (111), (202), (202), (113), (311), and (220), which support the creation of the monoclinic crystal structure for CuO Card N°. (JCPDS-01–089-5899)36.

As can be seen from the XRD patterns in Fig. 1, the sample displayed a similar peak position with 2θ values of 31.8°, 34.46°, 36.29°, 47.59°, 56.65°, 62.93°, 66.45°, 68.02°, 69.14°, 72.68°, 77.05° which have been credited to the crystal planes of (100), (002), (101), (012), (110), (013), (200), (112), (201), (004), and (011) respectively where ZnO NPs having a hexagonal crystal structure (Space group P 63 m c (186) and lattice parameters of a = 3.24940 Å c = 5.20380 Å) JCDPS Card N°. (96–900-4179)37. Crystallite diameters in the various samples ranged from 20.12 nm to 25.04 nm (Table 1).

To determine the potential phytochemical compounds responsible for the green synthesis of the nanoparticles, FT-IR analysis was employed on the synthesized powder of α-Fe2O3, CuO, and ZnO nanoparticles as well as the extract of Portulaca oleracea L. leaf.

In this study, bands in the IR spectra that are indicative of the functional groups of biomolecules involved in the creation and stability of nanoparticles were detected.

Figure 2 presents the FT-IR spectrum of a Portulaca oleracea L. leaf extract together with the synthesized spectra of α-Fe2O3, CuO, and ZnO nanoparticles. The FT-IR spectra of Portulaca oleracea L leaf extract is shown in Fig. 2 (a). This spectrum showed some peaks at 3300, 2363, 1639, and 636 cm−1. The O–H group stretching vibration is what causes the broad band to vibrate at 3300 cm−1 38. The band at 2336 cm−1 are the typical C–C stretching peaks. Peaks at 1639 cm−1 are associated with the stretching vibrations of the aromatics cycles C=C, CC, and CO39. Another band at 636 cm−1 can be attributed to C–O–H stretching of primary alcohols and C–H out of plane aromatic band40.

(a) FTIR spectra of Portulaca oleracea L. leaf Extract, α-Fe2O3, CuO, and ZnO NPs; (b). Zoomed view range (400 to 700 cm−1) of synthesized α-Fe2O3, CuO, and ZnO NPs.

By comparing the spectrum of the as α-Fe2O3, CuO, and ZnO nanoparticles each other, Fig. 2(b) shows a peek at 510, 460, and 440 cm−1, which, corresponding to the Fe–O, Cu–O, and Zn–O stretching band of α-Fe2O3, CuO, and ZnO NPs, respectively .

Also a disappearance of the absorbance bands 3300, 2363, 1639, and 636 cm−1 associated of phenolic compounds after synthesing α-Fe2O3, CuO, and ZnO NPs, leads us to proclaim that the leaves extract of Portulaca oleracea L. contains phytochemicals such as alcohols, aldehydes, alkanes, and epoxy groups or ether groups which can be responsible for the nucleation process to reduce precursor from M+ to M0.

The formation of α-Fe2O3, CuO, and ZnO NPs and their morphological dimensions were investigated using the SEM. The SEM images of the produced α-Fe2O3, CuO, and ZnO NPs are shown in Fig. 3 (a, c, e). Nearly all of them are found to be spherical or oval in shape. With a few widely scattered solitary particles. The particle size distribution histograms given in Fig. 3 (b, d, f) indicate that the average size distribution of biosynthesized α-Fe2O3, CuO, and ZnO NPs is largely around 80 nm. We can determine that the gathered particles are crystals by comparing their size to that of crystals.

SEM images and particle size distributions of green synthesized α-Fe2O3, CuO, and ZnO NPs: (a, b) α-Fe2O3, (c, d) CuO, and (e, f) pH = ZnO).

The energy dispersive X-ray analysis (EDAX) of α-Fe2O3, CuO, and ZnO nanoparticles is displayed in Fig. 4. The EDAX spectra of α-Fe2O3 nanoparticles is shown in Fig. 4(a), and the peaks correspond to Fe and O. The paste and grid utilized for the EDAX analysis are where the components Cl in the figure come from. Figure 4 (b,c) The EDAX analysis showed only obvious peaks for the elements Fr, Zn, and O; no other peaks could be found, indicating that the powder was manufactured without any impurities for the CuO and ZnO NPs sample.

EDS of (a) α-Fe2O3,(b) CuO,(c) and ZnO Nanoparticles.

Table 2 displays the weight, atomic, and error % percentages of nanoparticles of α-Fe2O3, CuO, and ZnO. This demonstrates that the Fe:O, Cu:O, and Zn:O ratios in synthetic nanoparticles are not stoichiometric or 1:1. CuO, ZnO, and α-Fe2O3 NPs.

The UV–Vis spectra of α-Fe2O3, CuO, and ZnO nanoparticles synthesized using a Portulaca oleracea L. Leaf extract are shown in Fig. 5(a). As can be seen from this figure, one peaks of maximum absorption are exhibited for every nanoparticle. The absorption peak at 291, 365, 260 nm gives a clue that α-Fe2O3, CuO, and ZnO nanoparticles, respectively.α-Fe2O3, CuO, and ZnO nanoparticles' estimated optical band gap (Eg) can be calculated by extrapolating from the absorption edge, which is provided by Tauc's relation41,42:

where \(h\) is the Planck constant, \(A\) is a constant, \(hv\) is the energy of light, n is a factor is equal to 1/2 or 2 for direct and indirect transition, and α is the absorption coefficient. Plotting \(\left( {\alpha h\nu } \right)^{2}\) and \(\left( {\alpha h\nu } \right)^{1/2}\) vs photon energy allows one to determine the optical bandgap energy for direct \({\text{E}}_{{{\text{g}}1}}^{{{\text{opt}}}}\) and indirect \(E_{g2}^{opt}\) transitions (hv). The value of \(E_{g}^{opt}\) is calculated by extrapolating to \(\left( {\alpha h\nu } \right)^{2} = 0\) for direct transition and \(\left( {\alpha h\nu } \right)^{1/2} = 0 \) for indirect transition in NPs of α-Fe2O3, CuO, and ZnO. The plot of \(\left( {\alpha h\nu } \right)^{2} \) and \(\left( {\alpha h\nu } \right)^{1/2}\) versus \(hv\) 23 is shown in Fig. 5 (b–c). The energy gap was calculated from the point where the energy axis and the edge of the linear portion of absorption met. The photon energy is equal to \(E_{g}^{opt}\) when \(\left( {\alpha h\nu } \right)^{n}\) is zero. Table 3 shows the samples' optical band gaps.

Optical properties of the α-Fe2O3, CuO, and ZnO NPs: UV–vis spectra (a); optical bandgap energy (b) ; indirect bandgap energy (c) transitions relying on Tauc’s method; (d) Urbach energy.

The band tail energy, sometimes called Urbach energy \(E_{u}\), can be seen in UV–vis spectra. It has been found that the Urbach energy \(E_{u}\) values decrease with crystal size in the case of α-Fe2O3, CuO, and ZnO NPs forms, leading to a decrease in crystallinity and structural disorder. Utilizing the reciprocal values of the slopes of the linear component of the \(\ln (a) \) vs photon energy \( h\nu\), the Urbach energy \(E_{u}\) is computed (Fig. 5d). According to Urbach (1953)43, the absorption coefficient and photon energy have an exponential relationship close to the band edge. Table 3 displays the calculated Urbach energy values for the samples.

The reciprocal of the slope of the linear fit section of the curve's photon energy was used to determine the Urbach energy \(E_{u}\). The latter is based on the energy difference between the ends of the valence and conduction band tails; the lower the energy, the less turbulence; however, the disorder may change depending on the presence of modifying oxides.

The rate of extraction of As(III), Be(II), Cd(II), Cr(VI), Mn(II), Mo(II), Ni(II), Pb(II), Sb(III), Se(-II), and Zn(II) by α-Fe2O3, CuO and ZnO NPs was studied by equilibrating the 20 g nanoparticles with a series of ion solutions for different time intervals. Figure 6 shows the amount of As, Be, Cd, Cr, Mn, Mo, Ni, Pb, Sb, Se, and Zn (Table 4) adsorbed at a contact time t (min). The results have indicated that ~ 80% of the adsorbed of heavy metals takes place in 5 and 10 min respectively, and the time required for both ions to reach a Mineralization percentage of 99.99% is less than 30 min shown in Fig. 6.

Time effect and efficiency rate of (a, b) α-Fe2O3, (c, d) CuO, and (e, f) ZnO for removal of heavy metals from the aqueous phase.

The adsorption behaviour described above can be explained on the basis of surface charge and proton competitive sorption. The increase in deprotonation induces the increase of negatively charged sites, which enhances attractive electrostatic interaction and ion exchange between the NPs sorbent surface and metal ions and consequently leads to the enhancement of the adsorption capacity. As shown in Fig. 7,

Schematic of the experiment and Mechanism of the transfer of an adsorbate to the adsorption site within a grain.

The knowledge of the parameters of the adsorption equilibrium makes it possible to deduce the adsorption capacities of a support. The determination of the kinetic parameters must, in addition, be the determination of the kinetic parameters must, in addition, be carried out for the prediction of the curves. The transfer of an adsorbate from the transfer of an adsorbate from the liquid phase to an adsorption site, represented by Fig. 7, involves the following steps:

1st step (the external diffusion): the transfer of solute molecules from the external liquid phase to the liquid phase bound to the adsorption site to the liquid phase bound to the solid particle (by diffusion and convection).

2nd step (the internal diffusion): the transfer of the solute through the liquid film towards the external surface of the adsorbent.

3rd step the diffusion of the adsorbate inside the particle of the adsorbent under the effect of the concentration gradient. The adsorbate molecule can diffuse from one adsorption site to another other either in the Free State (after desorption) in the intraparticle liquid phase (migration characterized by a diffusion coefficient Df), or in the adsorbed state, from an adsorption site towards an adjacent site (migration of surface characterized by a coefficient of diffusion Ds).

4th step adsorption (fixation).

The results obtained (Table 4) show that half an hour of stirring leads to a decrease in the concentration of all the metals present in the sample. By going from 10 min of agitation to 30 min, Note that by going from 5 to 30 min of agitation, we were able to completely get rid of most of the elements present in petroleum water percentages varying between 90 and 100% (see Fig. 6), thanks to the efficiency of the nanoparticles used to filter this oily water. This is due to the high quality of the specific surface of the absorbent material.

The photocatalytic process is an alternative and cutting-edge technique increasingly used to treat produced water. In this study, petroleum was used as a produced water indicator.

In Fig. 8 we discovered that 80% of the hydrocarbon degradation for photocatalyst NPS uses a UV sunlight source. The outcome also demonstrates that OIW deterioration was more pronounced when reactions for 30 min under visible light. Removing the (TSS) in the oily water by 70% as shown in Fig. 8, due to the quality of the surfaces of the three studied nanoparticles.

The photo-degradation rate hydrocarbon in oily water (OIW) and removing of Total Suspended Solids (TSS).

In the photocatalytic process, nanoparticles transform organic contaminants into CO2, H2O, and reactive oxidizing species like oxygen or air44. Nanoparticles are used in a wide range of industries45,46,47,48,49,50,51,52. When a photon with energy (hv) equal to or greater than the band gap of semiconductor photocatalytic nanoparticles is absorbed, the mechanism of the photocatalytic process is said to have begun53. Thus, positive holes (h+) and electrons (e−) are created on the surface of nanophotocatalysis as a result of electrons being transferred by photoabsorption from the valence band to the conduction band54. As a result, the interactions between positive holes in CB and water produce hydroxyl radicals (OH) Fig. 9.

illustrates the predicted reaction process for the photocatalytic breakdown of the pollutant's hydrocarbon.

Based on the previous discussions, Fig. 10 discusses a potential reaction pathway using the hydroxyl and superoxide radicals for the potential creation of intermediates. The primary oxidation step is thought to be started by hydroxy radicals, which are produced after photogenerated holes trapped at the α-Fe2O3, CuO, and ZnO NPs surface oxidize hydroxyl ions.

Mineralization mechanism by photodegradation of hydrocarbons (oily water) using nanoparticles.

The porous nanoparticles were utilized for the degradation of hydrocarbon in oily water (OIW) and remove Total Suspended Solids (TSS) and the total adsorption of heavy metals (Bi, Cr, Mo, Sb and Se). In addition about 80% of the hydrocarbon degradation for photocatalyst NPS uses a UV sunlight source. Mainly polyhydroxylated and carbonylated intermediates are formed, which are ultimately converted to carbon dioxide. The amount of CO as the final mineralization product. And it has proven that it can remove heavy metals and purify water from all suspended impurities, the potentiality exists for the application of photocatalytic methods in the purification of water polluted by hydrocarbons.

All data generated or analysed during this study are included in this published article.

Nanoparticles

Zinc oxide

Cupric oxide

Hematite

Oily in water

Total suspended solids

Hedar, Y. & Budiyono. Pollution impact and alternative treatment for produced water. E3S Web. Conf. 31, (2018).

Cherepovitsyn, A., Rutenko, E. & Solovyova, V. Sustainable development of oil and gas resources: A system of environmental, socio-economic, and innovation indicators. J.Marine Sci. Eng. vol. 9 (2021).

Islam, A., Ahmad, A. & Laskar, M. A. Characterization of a chelating resin functionalized via azo spacer and its analytical applicability for the determination of trace metal ions in real matrices. J. Appl. Polym. Sci. 123, 3448–3458 (2012).

Article CAS Google Scholar

Singh, A. et al. Heavy metal contamination of water and their toxic effect on living organisms. The Toxicity of Environ. Pollut. (eds. Dorta, D. J. & Oliveira, D. P. de) Ch. 2 (IntechOpen, 2022).:https://doi.org/10.5772/intechopen.105075.

Fakhru’l-Razi, A. et al. Review of technologies for oil and gas produced water treatment. J. Hazard. Mater. 170, 530–551 (2009).

Bouafia, A., Laouini, S. E., Khelef, A., Tedjani, M. L. & Guemari, F. Effect of ferric chloride concentration on the type of magnetite (Fe3O4) nanoparticles biosynthesized by aqueous leaves extract of Artemisia and assessment of their antioxidant activities. J. Clust. Sci. 32, 1033–1041 (2021).

Article CAS Google Scholar

Daoudi, H. et al. Secondary metabolite from nigella Sativa seeds mediated synthesis of silver oxide nanoparticles for efficient antioxidant and antibacterial activity. J. Inorg. Organomet. Polym. Mater. https://doi.org/10.1007/s10904-022-02393-y (2022).

Article Google Scholar

Alshawwa, S. Z. et al. In Situ Biosynthesis of Reduced Alpha Hematite (α-Fe2O3) Nanoparticles by Stevia Rebaudiana L. Leaf Extract: Insights into Antioxidant, Antimicrobial, and Anticancer Properties. Antibiotics 11, 1252 (2022).

Geneti, S. T. et al. Biogenic synthesis of magnetite nanoparticles using leaf extract of thymus schimperi and their application for monocomponent removal of chromium and mercury ions from aqueous solution. J. Nanomater. 2022, 1–15 (2022).

Article Google Scholar

Mthana, M. S., Mthiyane, D. M. N., Onwudiwe, D. C. & Singh, M. Biosynthesis of ZnO nanoparticles using capsicum Chinense fruit extract and their in vitro cytotoxicity and antioxidant assay. Appl. Sci. 12, 4451 (2022).

Article CAS Google Scholar

Gherbi, B. et al. Effect of pH value on the bandgap energy and particles size for biosynthesis of Zno nanoparticles: efficiency for photocatalytic adsorption of methyl orange. Sustainability vol. 14 (2022).

Hui, H. et al. Biosynthesis, characterization, and application of Cu2O nanoparticles originated from Cressa leaf extract as an efficient green catalyst in the synthesis of some chromenes. J. Iran. Chem. Soc. 19, 1261–1270 (2022).

Article CAS Google Scholar

Alsamhary, K., Al-Enazi, N. M., Alhomaidi, E. & Alwakeel, S. Spirulina platensis mediated biosynthesis of Cuo Nps and photocatalytic degradation of toxic azo dye Congo red and kinetic studies. Environ. Res. 207, 112172 (2022).

Article CAS PubMed Google Scholar

Zidane, Y. et al. Green synthesis of multifunctional MgO@AgO/Ag2O nanocomposite for photocatalytic degradation of methylene blue and toluidine blue. Front. Chem. 10, (2022).

Bouafia, A. et al. Plant-mediated synthesis of iron oxide nanoparticles and evaluation of the antimicrobial activity: A review. Mini. Rev. Org. Chem. 17, 1–11 (2020).

Google Scholar

Bouafia, A. & Laouini, S. E. Plant-mediated synthesis of iron oxide nanoparticles and evaluation of the antimicrobial activity: A review. Mini. Rev. Org. Chem. 17, 1–11 (2020).

Google Scholar

Wang, J. P., Ma, X. X., Fang, G. Z., Wang, S. & Yin, H. L. Determination of six heavy metals elements in drinking water by inductively coupled plasma mass spectrometry. Guang Pu Xue Yu Guang Pu Fen Xi/Spectroscopy Spectr. Anal. 30, 2827–2829 (2010).

Manousi, N., Isaakidou, E. & Zachariadis, G. A. An Inductively Coupled Plasma Optical Emission Spectrometric Method for the Determination of Toxic and Nutrient Metals in Spices after Pressure-Assisted Digestion. Appl. Sci. (Switzerland) vol. 12 (2022).

Terea, H., Selloum, D., Rebiai, A., Bouafia, A. & Ben Mya, O. Preparation and characterization of cellulose/ZnO nanoparticles extracted from peanut shells: Effects on antibacterial and antifungal activities. Biomass Convers. Biorefinery https://doi.org/10.1007/s13399-023-03959-7 (2023).

Article Google Scholar

Legmairi, S. et al. Biofabrication of NiO and NiO-decorated Fe nanocomposite efficiency for removal of methylene blue from aqueous solution. Biomass Convers. Biorefinery https://doi.org/10.1007/s13399-023-03912-8 (2023).

Article Google Scholar

Kir, I., Laouini, S. E., Meneceur, S., Bouafia, A. & Mohammed, H. A. M. Biosynthesis and characterization of novel nanocomposite ZnO/BaMg2 efficiency for high-speed adsorption of AZO dye. Biomass Convers. Biorefinery https://doi.org/10.1007/s13399-023-03985-5 (2023).

Article Google Scholar

Bouafia, A. & Laouini, S. E. Green synthesis of iron oxide nanoparticles by aqueous leaves extract of Mentha Pulegium L.: Effect of ferric chloride concentration on the type of product. Mater. Lett. 265, 127364 (2020).

Bouafia, A., Laouini, S. E., Tedjani, M. L., Ali, G. A. M. & Barhoum, A. Green biosynthesis and physicochemical characterization of Fe3O4 nanoparticles using Punica granatum L. fruit peel extract for optoelectronic applications (2021) https://doi.org/10.1177/00405175211006671.

Kumar, M. R. A. et al. Evaluation of bi-functional applications of ZnO nanoparticles prepared by green and chemical methods. J. Environ. Chem. Eng. 7, 103468 (2019).

Article CAS Google Scholar

Andualem, W. W., Sabir, F. K., Mohammed, E. T., Belay, H. H. & Gonfa, B. A. Synthesis of copper oxide nanoparticles using plant leaf extract of catha edulis and its antibacterial activity. J. Nanotechnol. 2020, 2932434 (2020).

Article Google Scholar

Belaiche, Y. et al. Green synthesis and characterization of silver/silver oxide nanoparticles using aqueous leaves extract of artemisia herba-alba as reducing and capping agents. Rev. Română Mater. Rom. J. Mater. 2021, 342–352.

Ben Amor, M. L., Zeghdi, S., Laouini, S. E., Bouafia, A. & Meneceur, S. pH reaction effect on biosynthesis of CuO/Cu2O nanoparticles by Moringa oleifera leaves extracts for antioxidant activities. Inorg. Nano-Metal Chem. 1–11 (2022) https://doi.org/10.1080/24701556.2022.2077376.

Abdullah, J. A. A. et al. Green synthesis and characterization of iron oxide nanoparticles by pheonix dactylifera leaf extract and evaluation of their antioxidant activity. Sustain. Chem. Pharm. 17, 100280 (2020).

Article Google Scholar

Al-Senani, G. M. & Al-Fawzan, F. F. Adsorption study of heavy metal ions from aqueous solution by nanoparticle of wild herbs. Egypt. J. Aquat. Res. 44, 187–194 (2018).

Article Google Scholar

Solanki, J. N. & Murthy, Z. V. P. Controlled size silver nanoparticles synthesis with water-in-oil microemulsion method: A topical review. Ind. Eng. Chem. Res. 50, 12311–12323 (2011).

Article CAS Google Scholar

Pemartin-Biernath, K. et al. Synthesis of mixed Cu/Ce oxide nanoparticles by the oil-in-water microemulsion reaction method. Materials (Basel). 9, (2016).

Fouda, A., Hassan, S. E. D., Saied, E. & Azab, M. S. An eco-friendly approach to textile and tannery wastewater treatment using maghemite nanoparticles (γ-Fe2O3-NPs) fabricated by Penicillium expansum strain (K-w). J. Environ. Chem. Eng. 9, 104693 (2021).

Article CAS Google Scholar

Amerian, T., Farnood, R., Sarathy, S. & Santoro, D. Effects of total suspended solids, particle size, and effluent temperature on the kinetics of peracetic acid decomposition in municipal wastewater. Water Sci. Technol. 80, 2299–2309 (2019).

Article CAS PubMed Google Scholar

Simopoulos, A. P., Norman, H. A., Gillaspy, J. E. & Duke, J. A. Common purslane: A source of omega-3 fatty acids and antioxidants. J. Am. Coll. Nutr. 11, 374–382 (1992).

Article CAS PubMed Google Scholar

Tsirelson, V. G., Antipin, M. Y., Strel’tsov, V. A., Ozerov, R. P. & Struchkov, Y. T. Distribution of electron density and the gradient of electrical field in hematite at 153 K from the precision X-ray diffraction data. in Doklady Akademii Nauk vol. 298 1137–1141 (Russian Academy of Sciences, 1988).

Massarotti, V., Capsoni, D., Bini, M., Altomare, A. & Moliterni, A. G. G. X-ray powder diffraction ab initio structure solution of materials from solid state synthesis: The copper oxide case. Zeitschrift für Krist.—Cryst. Mater. 213, 259–265 (1998).

Kihara, K. & Donnay, G. Anharmonic thermal vibrations in ZnO. Can. Mineral. 23, 647–654 (1985).

CAS Google Scholar

Abdellatif, A. A. H., Alturki, H. N. H. & Tawfeek, H. M. Different cellulosic polymers for synthesizing silver nanoparticles with antioxidant and antibacterial activities. Sci. Rep. 11, 1–18 (2021).

Article Google Scholar

Patil, R. B. & Chougale, A. D. Analytical methods for the identification and characterization of silver nanoparticles: A brief review. Mater. Today Proc. 47, 5520–5532 (2021).

Article CAS Google Scholar

Raj, A. et al. Green synthesis and charcterization of silver nanoparticles from leafs extracts of rosa indica and its antibacterial activity against human pathogen bacteria. Orient. J. Chem. 34, 326–335 (2018).

Article CAS Google Scholar

Lassoued, A., Lassoued, M. S., Dkhil, B., Ammar, S. & Gadri, A. Synthesis, structural, morphological, optical and magnetic characterization of iron oxide (α-Fe2O3) nanoparticles by precipitation method: Effect of varying the nature of precursor. Phys. E Low-dimensional Syst. Nanostruct. 97, 328–334 (2018).

Article ADS CAS Google Scholar

Soltan, W. Ben, Nasri, S., Lassoued, M. S. & Ammar, S. Structural, optical properties, impedance spectroscopy studies and electrical conductivity of SnO2 nanoparticles prepared by polyol method. J. Mater. Sci. Mater. Electron. 28, 6649–6656 (2017).

Urbach, F. The Long-wavelength edge of photographic sensitivity and of the electronic absorption of solids. Phys. Rev. 92, 1324–1324 (1953).

Article ADS CAS Google Scholar

Lee, K. M., Lai, C. W., Ngai, K. S. & Juan, J. C. Recent developments of zinc oxide based photocatalyst in water treatment technology: A review. Water Res. 88, 428–448 (2016).

Article CAS PubMed Google Scholar

Goodarzi, M. et al. Investigation of nanofluid mixed convection in a shallow cavity using a two-phase mixture model. Int. J. Therm. Sci. 75, 204–220 (2014).

Article CAS Google Scholar

Safaei, M. R., Ahmadi, G., Goodarzi, M. S., Kamyar, A. & Kazi, S. N. Boundary Layer Flow and Heat Transfer of FMWCNT/Water Nanofluids over a Flat Plate. Fluids vol. 1 (2016).

Yan, L., Xu, Z. & Zhang, J. Influence of nanoparticle geometry on the thermal stability and flame retardancy of high-impact polystyrene nanocomposites. J. Therm. Anal. Calorim. 130, 1987–1996 (2017).

Article CAS Google Scholar

Heydari, A. et al. The effect of attack angle of triangular ribs on heat transfer of nanofluids in a microchannel. J. Therm. Anal. Calorim. 131, 2893–2912 (2018).

Article CAS Google Scholar

Nasiri, H. et al. A smoothed particle hydrodynamics approach for numerical simulation of nano-fluid flows. J. Therm. Anal. Calorim. 135, 1733–1741 (2019).

Article CAS Google Scholar

Arani, A. A. A. et al. Heat transfer improvement of water/single-wall carbon nanotubes (SWCNT) nanofluid in a novel design of a truncated double-layered microchannel heat sink. Int. J. Heat Mass Transf. 113, 780–795 (2017).

Article CAS Google Scholar

Khodabandeh, E., Safaei, M. R., Akbari, S., Akbari, O. A. & Alrashed, A. A. A. A. Application of nanofluid to improve the thermal performance of horizontal spiral coil utilized in solar ponds: Geometric study. Renew. Energy 122, 1–16 (2018).

Article CAS Google Scholar

Sheikholeslami, M. & Shehzad, S. A. CVFEM simulation for nanofluid migration in a porous medium using Darcy model. Int. J. Heat Mass Transf. 122, 1264–1271 (2018).

Article CAS Google Scholar

Liu, B., Chen, B. & Zhang, B. Oily wastewater treatment by nano-tio2-induced photocatalysis: seeking more efficient and feasible solutions. IEEE Nanotechnol. Mag. 11, 4–15 (2017).

Article Google Scholar

Umar, K., Ibrahim, M. N. M., Ahmad, A. & Rafatullah, M. Synthesis of Mn-doped TiO2 by novel route and photocatalytic mineralization/intermediate studies of organic pollutants. Res. Chem. Intermed. 45, 2927–2945 (2019).

Article CAS Google Scholar

Download references

Department of Process Engineering, Faculty of Technology, University of El Oued, 39000, El-Oued, Algeria

Abderrhmane Bouafia, Souhaila Meneceur, Salah Eddine Laouini, Souheila Legmairi & Hamdi Ali Mohammed Mohammed

Laboratory of Biotechnology Biomaterial and Condensed Matter, Faculty of Technology, University of El Oued, 39000, El-Oued, Algeria

Abderrhmane Bouafia, Souhaila Meneceur, Salah Eddine Laouini, Henda Daoudi, Souheila Legmairi & Hamdi Ali Mohammed Mohammed

Laboratory of Polymers Treatment & Forming, Faculty of Technology, M’Hamed Bougara University, 35000, Boumerdes, Algeria

Souheyla Chami

Laboratory of Bioresources, Integrative Biology and Exploiting, Biotechnology Higher Institute, Monastir University, 5000, Monastir, Tunisia

Henda Daoudi

Department of Chemistry, Faculty of Exact Sciences and Informatics, University of Jijel, 18000, Jijel, Algeria

Narimene Aoun

Department of Nanomedicine and Advanced Technologies, CIC-Fluorotronics, Inc., San Diego, CA, 92037, USA

Farid Menaa

You can also search for this author in PubMed Google Scholar

Conceptualization, A.B., S.C., S.E.L., S.M., F.M. and H.D.; methodology, A.B., S.C., S.M., F.M. and N.A.; validation, A.B., S.C., S.E.L., S.M., F.M. and N.A.; investigation, H.A.M.M., N.A., F.M. and S.M.; resources, S.C., A.B., and F.M.; data curation, S.C., A.B., N.A., F.M. and M.S.; writing—original draft preparation, S.E.L., S.M., H.A.M.M., N.A., F.M. and H.A.M.M.; writing—review and editing, H.A.M.M., S.M., N.A., F.M. and H.D.; supervision, H.A.M.M., S.E.L., S.M., F.M. and H.D. All authors have read and agreed to the published version of the manuscript.

Correspondence to Abderrhmane Bouafia.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Bouafia, A., Meneceur, S., Chami, S. et al. Removal of hydrocarbons and heavy metals from petroleum water by modern green nanotechnology methods. Sci Rep 13, 5637 (2023). https://doi.org/10.1038/s41598-023-32938-1

Download citation

Received: 23 January 2023

Accepted: 05 April 2023

Published: 06 April 2023

DOI: https://doi.org/10.1038/s41598-023-32938-1

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

Reaction Kinetics, Mechanisms and Catalysis (2023)

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.